Adhesive Lined Cross-Linked Polyolefin Heat Shrink Tape
Product Description
WRSJD: Adhesive Lined Cross-Linked Polyolefin Heat Shrink Tape
• Fully Shrink Temperature: 120ºC
• Continuous Operating Temperature: -45ºC to 125ºC
• Features:
• Eliminates air leakage in vacuum and ventilation systems.
• Seals against moisture ingress and other contaminants.
• Powerful adhesive bonds to galvanized steel, aluminum, and stainless steel.
• Effective, reproducible seal allows for resistance to bending, vibrations, and other mechanical stresses over a wide range of temperatures.
• Application procedure is quick, simple, and clean.
• Color: Black, Red, Green, Yellow.
• Technical Data:
• Tensile Strength: ≥10.4 MPa (ASTM D2671), Typical Performance: 11.5 MPa
• Elongation: ≥300% (ASTM D2671), Typical Performance: 450%
• Tensile Strength after aging (MPa): ≥7.3 (UL224 158ºC×168hr), Typical Performance: 8.0 MPa
• Elongation after aging (%): ≥200 (UI224 158ºC×168hr), Typical Performance: 35%
• Dielectric Strength: ≥15 kV/mm (IEC243), Typical Performance: 17.5 kV/mm
• Volume Resistivity: ≥1x10^14 Ω·cm (ASTM D876), Typical Performance: 2.5X10^14 Ω·cm
• Adhesive Properties:
• Water Absorption: ≤0.2% (ASTM D570)
• Softening Point: 95ºC (ASTM E28)
• Strength of Peeling (PE): 120N/25mm (ASTM D 1000)
• Strength of Peeling (AL): 80N/25mm (ASTM D 1000)
|
Technical Data
| Property |
Test Method |
Standard |
Typical Performance |
| Tensile Strength(MPa) |
ASTM D2671 |
≥10.4 |
11.5 |
| Elongation(%) |
ASTM D2671 |
≥300 |
450 |
| Tensile Strength after aging (MPa) |
Ul224 158ºC X168hr |
≥7.3 |
8.5 |
| Elongation after aging(%) |
Ul224 158ºC X168hr |
≥200 |
350 |
| Dieletric strength(kv/mm) |
IEC 243 |
≥15 |
17.5 |
| Volume resistivity(Ω.cm) |
ASTM D 876 |
≥1X1014 |
2.5X1014 |
Adhesive
| Property |
Test Method |
Standard |
| Water Absorption |
ASTM D570 |
≤0.2% |
| Sofening Point (ºC) |
ASTM E28 |
95 |
| Strength of peeling(PE) |
ASTM D 1000 |
120N/25mm |
| Strength of peeling(AL) |
ASTM D 1000 |
80N/25mm |
|