Manufactured from: Cross-linked polyolefin, inner coated with adhesive,urpose: Protecting against accidental flashover.
Usage: Used in medium voltage cable terminations up to 42 kV.
Shrink temperature: Starts at 90ºC, fully recovers at 130ºC.
Color: Red.
| Spec. |
As Supplied(mm) |
After Recovered |
| Inner Diameter Min |
Wall Thickness(±0.3) |
Inner Diameter Max |
Wall Thickness(T:±0.3) |
| ALRSJG-30/12 |
30 |
1.0 |
12 |
2.2 |
| ALRSJG-35/14 |
35 |
1.0 |
14 |
2.3 |
| ALRSJG-40/17 |
40 |
1.0 |
17 |
2.3 |
| ALRSJG-50/22 |
50 |
1.0 |
22 |
2.5 |
| ALRSJG-35/13 |
35 |
1.2 |
13 |
3.0 |
| ALRSJG-40/15 |
40 |
1.2 |
15 |
3.0 |
| ALRSJG-50/19 |
50 |
1.1 |
19 |
3.0 |
| ALRSJG-55/24 |
55 |
1.4 |
24 |
3.2 |
| ALRSJG-60/26 |
60 |
1.4 |
26 |
3.2 |
| ALRSJG-70/29 |
70 |
1.4 |
29 |
3.2 |
| ALRSJG-75/35 |
75 |
1.5 |
35 |
3.2 |
| ALRSJG-80/36 |
80 |
1.4 |
36 |
3.2 |
| ALRSJG-90/41 |
90 |
1.6 |
41 |
3.5 |
| ALRSJG-100/45 |
100 |
1.5 |
45 |
3.5 |
| Property |
Test Method |
Standard Value |
| Tensile Strength |
ASTM-D-638 |
≥8MPa |
| Elongation at Break |
ASTM-D-638 |
300% |
| Changes in Tensile Breaking Strength After Heat Aging |
ASTM-D-5510 |
≤±30% |
| Volume Resistivity |
IEC 60093 |
1x1014Ωcm |
| Dielectric Strength |
IEC 60243 |
≥20kV/mm |
| Tracking Resistance |
IEC 60587 |
1A 3.5 |
| Dielectric Constant |
IEC 60250 |
≤5 |
| Heat Shock |
160°C,4h |
No Crack |
| Water Absorption |
ISO 62 |
≤0.1% |
| Hardness(Shore A) |
IS0 868 |
≤80 |
| Brittle Temperature |
IS0 974 |
-40ºC |