Made of cross linked polyolefin to provide mechanical protection and strain relief.
Inner coated with adhesive on the body and the fingers to form a durable watertight seal.
To provide sealing protection over 6-core cable crutch, such as trailing cable, variable frequency drive cable,telecommunication cables,control cable,etc.
Shrink temperature:start at 90ºC,and fully recovered at 130ºC.
The company has imported and domestic rubber injection molding machine, vacuum automatic pressure gel molding machine, rubber mixer, high-pressure testing equipment, polymer testing equipment.
| Cores |
Spec. |
As Supplied(mm) |
After Recovered |
| Body |
Big |
Small |
Full |
Body |
Big |
Small |
| Diameter |
Finger |
Finger |
Length |
Diameter |
Finger |
Finger |
| (D) |
Diameter |
Diameter |
(L) |
(D) |
Diameter |
Diameter |
| Min |
(d1) |
(d2) |
(±5) |
Max |
(d1) |
(d2) |
| |
Min |
Min |
|
|
Max |
Max |
| 6-cores |
1# |
84 |
30 |
20 |
215 |
41 |
11 |
8 |
| Breakout |
2# |
132 |
55 |
31 |
215 |
53 |
16 |
11 |
| Property |
Test Method |
Standard Value |
| Tensile Strength |
ASTM-D-638 |
≥12MPa |
| Elongation at Break |
ASTM-D-638 |
≥300% |
| Volume Resistivity |
IEC 60093 |
≥1x1013Ω.cm |
| Dielectric Strength |
IEC 60243 |
≥15kV/mm |
| Brittle Temperature |
ISO 974 |
-40ºC |
| Heat Shock |
160ºC,4h |
No Crack |
| Water Absorption(23±2)ºC 24h |
ISO 62 |
≤0.1% |
| Hardness(Shore A) |
ISO 868 |
≥80 |