Heat Shrink Repair Sleeve for Fast and Permanent Repair and Sealing Protection

• Customization: Available
• Application: Telecommunication
• Voltage: Low and Medium Voltage Cable
• Model NO.: Heat shrink repair sleeve
• Insulation Material: PE
• Sheath Material: PVC
• Material Shape: Round Wire
• Wire Core Material: Tinned Wire
• Certification: ISO
• Model: Wrap Aournd Sleeves
• Transport Package: Bags, Cartons
• Trademark: YQALT
• Origin: China
• HS Code: 3917310000
• Production Capacity: 1, 000, 000 Set/Month

Product Description

Heat shrink repair sleeve

Overview

Manufactured from: Polyolefin, inner coated with hot-melt adhesive.
Purpose: Providing fast and permanent repair and sealing protection for power cables.
Features: High tensile strength, abrasion, and corrosion resistance.
Installation: A corrosion-proof metal channel is used to close the sleeve during
installation.
Shrink temperature: Starts at 90°C, fully recovers at 130°C.

 

Selection Table

Spec.	As Supplied(mm)		After Recovered
	Width(W)Min	Wall Thickness(T:+0.3)	Width (W)Max	Wall Thickness(T:±0.3)
ALRSXP-30/12	120	1.3	38	3.8
ALRSXP-40/12	130	1.2	38	3.8
ALRSXP-50/17	160	1.3	53	3.8
ALRSXP-65/24	205	1.2	75	3.8
ALRSXP-85/27	270	1.3	82	3.8
ALRSXP-100/27	320	1.4	82	3.8
ALRSXP-120/40	380	1.4	129	3.8
ALRSXP-150/50	475	1.4	157	3.8
ALRSXP-160/50	505	1.3	157	3.8
ALRSXP-170/51	535	1.2	160	3.8
ALRSXP-180/51	565	1.1	160	3.8
ALRSXP-195/52	590	1	163	3.8

Product Parameters

 

Property	Test Method	Standard Value
Tensile Strength	ASTM-D-638	≥12MPa
Elongation at Break	ASTM-D-638	≥300%
Changes in Tensile Breaking Strength After Heat Aging	ASTM-D-5510	≤±20%
Dielectric Strength	IEC 60243	≥15kV/mm
Volume Resistivity	IEC 60093	≥1x1013Ω.cm
Heat Shock	160C,4h	No Crack
Water Absorption	ISO 62	≤0.1%
Hardness(Shore A)	ISO 868	≥80
Longitudinal Shrinkage	ASTM-D-2671	≤10%
Brittle Temperature	ISO 974	-40ºC
Eccentricity	ASTM-D-2671	≤30%