Heat Shrinkable Identification Sleeves
Product Description
RSFR: Heat Shrinkable Identification Sleeves
• Standards: SAE-AS 81531, MIL-STD-202F/Method 215J, UL224, RoHS
• Features:
• The sleeving is fabricated from irradiated, thermally stabilized, and flame-retarded modified polyolefin compound containing no halogens or cadmium.
• Application range: commercial, industrial environment.
• Operating temperature range: -55ºC to +125ºC
• Minimum recovery temperature: +125ºC
• Maximum storage temperature: +50ºC
• Shrink ratio: 2:1, 3:1
• Color: White, Yellow (other colors available if ordered).
• Printing mode: Single-sided and Double-sided printing formats available.
• Supplied mode: Either Continuous type or Ladder format type.
• Recommended Printers: Thermal transfer printer.
• Recommended Ribbons: N85 resin ribbon, Black, 100mm(width)×300m(length).
• Technical Data:
• Tensile Strength: 10.3 MPa (Testing Requirement), 14.3 MPa (WOER Results)
• Ultimate Elongation: ≥200% (Testing Requirement), 330% (WOER Results)
• Low temperature flexibility: 4 hours at -55±1ºC, No cracking
• Dielectric Strength: 19.7 kV/mm (Testing Requirement), 20 kV/mm (WOER Results)
• Volume Resistivity: 10^14 Ω·cm (Testing Requirement), 2.0×10^14 Ω·cm (WOER Results)
• Corrosive effect: No corrosive
• Heat aging: 168 hours at 158±2ºC, No cracking, print is legible
• Print performance: Rubs (SAE-AS 81531, legible after 100 rubs), Strokes (MIL-STD-202F, legible after 100 strokes)
Features
| Material |
The sleeving shall be fabricated from irradiated, thermally stabilized and flame retarded modified PVDF |
| Application range |
Aerospace, defense and mass transit industries. |
| Operating temperature range |
-55~+225ºC |
| Minimum recovery temperature |
+150 ºC |
| Maximum storage temperature |
+50 ºC |
| Shrink ratio |
2:1 |
| Color |
White, Yellow, other color is available if ordered |
| Printing mode |
Single sided printing and Double sided printing formats available |
| Supplied mode |
Either Continuous type or Ladder format type is available |
| Recommended Printers |
Thermal transfer printer |
| Recommended Ribbons |
N95 resin ribbon, Black, 100mm(width)*300m(length) |
Key Properties
| Property |
Unit |
Requirement |
Test Method |
| Size |
mm |
As supplied |
ASTM D 2671 |
| Longitudinal Change |
% |
-10~+5 |
ASTM D 2671 |
| Tensile Strength |
MPa |
≥24.1 |
ASTM D 2671 |
| Ultimate Elongation |
% |
≥300 |
ASTM D 2671 |
| Specific Gravity |
g/cm3 |
≤1.9 |
ASTM D 2671 |
| Low Temperature Flexibility( -55ºC , 4h ) |
- |
No Cracks |
AMS-DTL-23053 |
| Heat Shock ( 275 ºC , 4h ) |
- |
No cracking, flowing or dripping |
ASTM D 2671 |
| Tensile Strength after Heat Aging ( 225ºC , 168h ) |
MPa |
≥19.1 |
ASTM D 2671 |
| Ultimate Elongation after Heat Aging ( 225ºC , 168h ) |
% |
≥200 |
ASTM D 2671 |
| Dielectric Strength |
Kv/mm |
≥15.7 |
ASTM D 2671 |
| Volume Resistivity |
Ω·cm |
≥1012 |
ASTM D 2671 |
| Corrosive Effect ( 160ºC , 16h ) |
- |
No corrosion |
ASTM D 2671 |
| Flammability |
- |
Pass |
UL224 VW-1, ASTM D 2671 |
| Water Absorption ( 23ºC , 24h ) |
% |
≤0.5 |
ISO 846 Procedure B |
| Print Permanence |
- |
Print legible after 50 rubs |
SAE AS81531 |
| Print Permanence after Heat Aging ( 225ºC , 168h ) |
- |
Print legible after 50 rubs |
SAE AS81531 |
| Print Permanence after Fluid Resistance |
- |
Print legible after 50 rubs |
MIL-STD-202F, method 215J |
|