Manufactured from: Cross-linked polyolefin.
Purpose: Providing effective electrical stress control for MV cable terminations and joints up to 42 kV.
Continuous operation temperature: -40C to 100C.
Shrink temperature: Starts at 90°C, fully recovers at 130°C.
Color: Black.
| Property | Test Method | Standard Value |
| Tensile Strength | ASTM-D-638 | ≥10MPa |
| Elongation at Break | ASTM-D-638 | ≥350% |
| Changes in Tensile Breaking Strength After Heat Aging | ASTM-D-5510 | ≤+20% |
| Volume Resistivity | IEC 60093 | ≥1X10¹ºΩ.cm |
| Dielectric Constant | IEC 60250 | ≥15 |
| Hardness(Shore A) | ISO 868 | ≥80 |
| Longitudinal Shrinkage | ASTM-D-2671 | ≤5% |
| Eccentricity | ASTM-D-2671 | ≤30% |
| Spec. | As Supplied(mm) | After Recovered | ||
| Inner Diameter (D) Min | Wall Thickness(±0.3) | Inner Diameter (D) Max | Wall Thickness(±0.3) | |
| ALRSYL-30/11 | 30 | 0.8 | 11 | 2 |
| ALRSYL-35/14 | 35 | 0.8 | 14 | 2 |
| ALRSYL-40/17 | 40 | 0.8 | 17 | 2 |
| ALRSYL-45/20 | 45 | 0.8 | 20 | 2 |
| ALRSYL-50/22 | 50 | 1.2 | 22 | 2.6 |
| ALRSYL-55/24 | 55 | 1.4 | 24 | 3.3 |
| ALRSYL-60/29 | 60 | 1.3 | 29 | 3.3 |
| ALRSYL-70/29 | 70 | 1.3 | 29 | 3.3 |
| ALRSYL-80/29 | 80 | 1.2 | 29 | 3.3 |
| ALRSYL-95/42 | 95 | 1.4 | 42 | 3.6 |