Heat Shrink Insulation Connectors:
Product Description
SBRS-DZ: Heat Shrink Insulation Connectors
• Shrink Ratio: 4:1
• Minimum Shrink Temperature: 80ºC
• Continuous Operating Temperature: -45ºC to 125ºC
• Features:
• Exceptional clarity for visual confirmation of seal.
• Seals and protects against water, corrosive compounds, moisture, and contaminants.
• Tough, durable heat shrink tubing resists abrasion, crimp tool damage, and splitting.
• Shrinks 40% faster than nylon, preventing issues.
• Inner adhesive bonds to plastics, rubbers, and metals.
• Meets and conforms to OEM wiring specifications for installation and repairs.
• Technical Data:
• Tensile Strength: ≥14 MPa (ASTM D2671)
• Elongation: ≥200% (ASTM D2671)
• Tensile Strength after aging (MPa): ≥7.3 (UL224 158ºC×168hr)
• Elongation after aging (%): ≥100 (UI224 158ºC×168hr)
• Dielectric Strength: ≥15 kV/mm (IEC 60243)
• Volume Resistivity: ≥1x10^14 Ω·cm (IEC 60093)
• Adhesive Properties:
• Water Absorption: ≤0.5% (ASTM D570)
• Softening Point: 95±5ºC (ASTM E28)
• Strength of Peeling (PE): 120N/25mm (ASTM D 1000)
• Strength of Peeling (AL): 80N/25mm (ASTM D 1000)
Property |
Test Method |
Standard |
Tensile Strength(MPa) |
ASTM D2671 |
≥14 |
Elongation(%) |
ASTM D2671 |
≥200 |
Tensile Strength after aging (MPa) |
Ul224 158ºCX168hr |
≥7.3 |
Elongation after aging(%) |
Ul224 158ºCX168hr |
≥100 |
Dieletric strength(kV/mm) |
IEC 60243 |
≥15 |
Volume resistivity(Ω.cm) |
IEC 60093 |
≥1X1014 |
Adhesive
Property |
Test Method |
Standard |
Water Absorption |
ASTM D570 |
<0.5% |
Sofening Point (ºC) |
ASTM E28 |
95±5 |
Strength of peeling(PE) |
ASTM D 1000 |
120N/25mm |
Strength of peeling(AL) |
ASTM D 1000 |
80N/25mm |
|