Manufactured from cross linked semi-conductive polyolefin. Shrink temperature: start at 90ºC, and fully recovered at 130ºC. Color: black.
| Property | Test Method | Standard Value |
| Tensile Strength | ASTM-D-638 | ≥10MPa |
| Elongation at Break | ASTM-D-638 | ≥350% |
| Tensile Strength Variation After Heat Aging(130ºCx168h) | ASTM-D-5510 | ≤±20% |
| Elongation at Break Variation After Heat Aging(130ºCx168h) | ASTM-D-5510 | ≤±20% |
| Volume Resistivity | IEC 60093 | ≥1x103Ω.cm |
| Hardness(Shore A) | ISO 868 | ≥80 |
| Heat Shock | 160ºC,4h | No Crack |
| Brittle Temperature | ISO 974 | -40ºC |
| Longitudinal Shrinkage | ASTM-D-2671 | ≤10% |
| Spec. | As Supplied/mm | After Recovered/mm | Standard | Standard | ||
| Cut | Continuous | |||||
| Length/mm | Length | |||||
| Inner | Wall | Inner | Wall | (m/roll) | ||
| Diameter | Thickness | Diameter | Thickness | |||
| Min | (±0.3) | Max | (±0.3) | |||
| WRSBG-45/17 | 45 | 0.9 | 17 | 2.3 | 400-1200 | 25 |
| WRSBG-50/20 | 50 | 0.9 | 20 | 2.3 | 400-1200 | 25 |
| WRSBG-55/23 | 55 | 0.9 | 23 | 2.3 | 400-1200 | 25 |
| WRSBG-60/24 | 60 | 0.9 | 24 | 2.3 | 400-1200 | 25 |
| WRSBG-65/25 | 65 | 0.8 | 25 | 2.3 | 400-1200 | 25 |
| WRSBG-75/29 | 75 | 1 | 29 | 2.7 | 400-1200 | 25 |
| WRSBG-90/30 | 90 | 0.8 | 30 | 2.7 | 400-1200 | 25 |
| WRSBG-100/36 | 100 | 0.9 | 36 | 2.7 | 400-1200 | 15 |
| WRSBG-120/37 | 120 | 0.8 | 37 | 2.7 | 400-1200 | 15 |
| WRSBG-150/55 | 150 | 0.8 | 55 | 3.4 | 400-1200 | 15 |